Hot-selling Copper Tape Shielding - RTF ED Copper Foil – CIVEN
Hot-selling Copper Tape Shielding - RTF ED Copper Foil – CIVEN Detail:
Product Introduction
Reverse treated electrolytic copper foil (RTF) is a copper foil that has been roughened to varying degrees on both sides. This strengthens the peel strength of both sides of the copper foil, making it easier to use as an intermediate layer for bonding to other materials. Moreover, the different levels of treatment on both sides of the copper foil make it easier to etch the thinner side of the roughened layer. In the process of making a printed circuit board (PCB) panel, the treated side of the copper is applied to the dielectric material. The treated drum side is rougher than the other side, which constitutes a greater adhesion to the dielectric. This is the main advantage over standard electrolytic copper. The matte side does not require any mechanical or chemical treatment prior to the application of photoresist. It is already rough enough to have good laminating resist adhesion.
Specifications
CIVEN can supply RTF electrolytic copper foil with nominal thickness of 12 to 35µm up to 1295mm width.
Performance
The high temperature elongation reversed treated electrolytic copper foil is subjected to a precise plating process to control the size of the copper tumors and distribute them evenly. The reversed treated bright surface of the copper foil can significantly reduce the roughness of the copper foil pressed together and provide sufficient peel strength of the copper foil. (See Table 1)
Applications
Can be used for high-frequency products and inner laminates, such as 5G base stations and automotive radar and other equipment.
Advantages
Good bonding strength, direct multi-layer lamination, and good etching performance. It also reduces the potential for short circuit and shortens the process cycle time.
Table 1. Performance
|
Classification |
Unit |
1/3OZ (12μm) |
1/2OZ (18μm) |
1OZ (35μm) |
|
|
Cu Content |
% |
min. 99.8 |
|||
|
Area Weigth |
g/m2 |
107±3 |
153±5 |
283±5 |
|
|
Tensile Strength |
R.T.(25℃) |
Kg/mm2 |
min. 28.0 |
||
|
H.T.(180℃) |
min. 15.0 |
min. 15.0 |
min. 18.0 |
||
|
Elongation |
R.T.(25℃) |
% |
min. 5.0 |
min. 6.0 |
min. 8.0 |
|
H.T.(180℃) |
min. 6.0 |
||||
|
Roughness |
Shiny(Ra) |
μm |
max. 0.6/4.0 |
max. 0.7/5.0 |
max. 0.8/6.0 |
|
Matte(Rz) |
max. 0.6/4.0 |
max. 0.7/5.0 |
max. 0.8/6.0 |
||
|
Peel Strength |
R.T.(23℃) |
Kg/cm |
min. 1.1 |
min. 1.2 |
min. 1.5 |
|
Degraded rate of HCΦ(18%-1hr/25℃) |
% |
max. 5.0 |
|||
|
Change of color(E-1.0hr/190℃) |
% |
None |
|||
|
Solder Floating 290℃ |
Sec. |
max. 20 |
|||
|
Pinhole |
EA |
Zero |
|||
|
Preperg |
—- |
FR-4 |
|||
Note: 1. The Rz value of copper foil gross surface is the test stable value, not a guaranteed value.
2. Peel strength is the standard FR-4 board test value (5 sheets of 7628PP).
3. Quality assurance period is 90 days from the date of receipt.
Product detail pictures:
Related Product Guide:
Our enhancement depends around the sophisticated devices ,exceptional talents and repeatedly strengthened technology forces for Hot-selling Copper Tape Shielding - RTF ED Copper Foil – CIVEN , The product will supply to all over the world, such as: Turkey, Niger, Philippines, To meet the requirements of specific customers for each bit more perfect service and stable quality merchandise. We warmly welcome customers around the world to visit us, with our multi-faceted cooperation, and jointly develop new markets, create a brilliant future!
By Genevieve from Mauritania - 2018.02.21 12:14
We have been cooperated with this company for many years, the company always ensure timely delivery ,good quality and correct number, we are good partners.
By Lilith from Florence - 2017.02.18 15:54
Products categories
-
Manufacturer of Bcf Copper Foil - High-precisi...
-
Chinese wholesale Double Sided Conductive Tape ...
-
Top Suppliers Self Adhesive Aluminium Foil Shee...
-
Wholesale Discount Battery Nickel Foil - Good ...
-
One of Hottest for Silver Backed Copper Foil -...
-
Wholesale Dealers of Pure Copper Tape - RA Cop...